Beilstein J. Nanotechnol.2016,7, 1010–1017, doi:10.3762/bjnano.7.93
; copper(II) oxide; core–shell; reduced graphene oxide; Introduction
In the last years, graphene oxide (GO) and reduced graphene oxide (rGO) have emerged as suitable candidates to prepare graphene-based nanocomposites [1][2], including those based on GO/inorganic nanoparticles [3]. The opportunity to
PDF
Figure 1:
FE-SEM images of the copper foil (a) before and (b) after GO was deposited and dried at 80 °C. The ...
Beilstein J. Nanotechnol.2014,5, 789–800, doi:10.3762/bjnano.5.91
electrochemically synthesized product, P5, was nanometer-scaled powder of copper(II) oxide composed of highly branched nanoparticles [16]. Briefly, SEM data (Figure S2a, Supporting Information File 1) show that multi-armed nanoparticles were made of 500–1000 nm long radiating nano-spicules with a Cu/O ratio of
PDF
Figure 1:
SEM micrograph of CuO nanorods (PS2) at a) 5000× and b) 40000×. c) EDX spectrum of the as-synthesiz...